 JLC Electromet |  |
 |
 | ||
NICKEL ALLOYS - Grades for Electrical and Electronic ApplicationsNickel 200/201 is most widely used grade, generally specified for transistor caps, anodes for electronic tubes, leads of electronic components / Lead-in-Wires for lamps and for Wire-Mesh. Also used in strip form for various applications including Ni-Cd batteries.
Nickel 205 is also used for similar applications as Ni 200, mostly where higher purity and conductivity is required; inner parts of bulbs and electron tubes.
Nickel 200, 201 and 205 are supplied in the following conditions:
Alloy |
Ni% |
Mn% |
Fe% |
Si% |
Cu% |
C% |
Ti% |
|---|---|---|---|---|---|---|---|
Nickel 200 |
Min 99.2 |
Max 0.30 |
Max 0.2 |
Max 0.10 |
Max 0.20 |
Max 0.10 |
Max 0.10 |
Nickel 201 |
Min 99.2 |
Max 0.30 |
Max 0.2 |
Max 0.10 |
Max 0.20 |
Max 0.02 |
Max 0.10 |
Nickel 205 |
Min 99.6 |
Max 0.20 |
Max 0.2 |
Max 0.10 |
Max 0.10 |
Max 0.05 |
Max 0.05 |
Nickel 205 LC |
Min 99.6 |
Max 0.20 |
Max 0.2 |
Max 0.10 |
Max 0.10 |
Max 0.02 |
Max 0.05 |
| British Standard | Werkstoff Nr | UNS Designation | |
|---|---|---|---|
| Nickel 200/201 | BS 3075 (NA11) | 2.4060 | N 02200/01 |
| Nickel 205/205 LC | - | 2.4061 | N 02205 |
Wires: 8.0mm diameter to 0.122mm diameter. (0.315” diameter to 0.0048” diameter).
Strips: Width 0.4-100mm, Thickness: 0.10mm and above.
| Nickel 200/201 | Nickel 205/205 LC | |
|---|---|---|
| Density (g/cm³) | 8.89 | 8.89 |
| Thermal Conductivity (W/mk) | 70.20 | 75.00 |
| Thermal expansion 20-95°C (0.0000010/K ) | 13.30 | 13.30 |
| Electrical Resistivity at 20°C (µΩ-cm) | 9.00 | 8.90 |
| Nickel 200/201 | Nickel 205/205 LC | |
|---|---|---|
| Cold Drawn Annealed (N/mm²) | 500 | 450 |
| Elongation % (minimum) | 30 | 30 |
Note: Other Grades of Nickel and Nickel base alloys are also available. Please contact us for more information.